雙組份中空玻璃打膠機的市場前景！
我們知道中空玻璃雙組份膠的主膠A組份本身是不固化的,只有配合一定量的硫化劑以后才會逐步固化,為適當加快膠的固化速度,我門在膠的固化劑中加入一定量的硫化促進劑來加快硫化劑跟主膠的反應速度。
We know that the main rubber component a of the insulating glass two-component rubber itself is not cured. It will be gradually cured only after a certain amount of curing agent is added. In order to appropriately speed up the curing speed of the rubber, we add a certain amount of curing accelerator to the curing agent to speed up the reaction speed between the curing agent and the main rubber.
當我們人為地為了加速膠的固化而加大固化劑用量比例時,膠雖然提高了硫化的速度但膠的本身質量卻降低了,我們用刀片破開經加速硫化而固化的膠發現,這時的膠要比正常的膠松軟的多,像發泡的海綿.故我們的工人在調配雙組份膠時為了盡可能的保證膠的質量,一定要按標準的比例并充分混均以防止膠局部促進劑含量偏高從而影響中空玻璃的整體質量.
When we artificially increase the proportion of curing agent in order to accelerate the curing of rubber, although the curing speed of rubber is improved, the quality of rubber itself is reduced. We use a blade to break the rubber cured by accelerated curing. It is found that the rubber at this time is much softer than the normal rubber, like a foaming sponge. Therefore, in order to ensure the quality of rubber as much as possible when preparing two-component rubber, It must be fully mixed according to the standard proportion to prevent the high content of local accelerator from affecting the overall quality of insulating glass
中空玻璃雙組份膠所用的原料，都具有很強的粘結力，但不管粘結力多強的材料其特性都需要特定的符合性能要求的條件下才能實現，我們所用的雙組份膠它的*佳粘結力的產生(跟玻璃及鋁條)是在其加入規定量固化劑后立即涂在所需涂布的部位讓其在所涂布的部位完成從開始硫化———完全硫化的一個過程，如果我們將膠在半硫化狀態下在涂所需部位，則粘結強度就大有影響。
The raw materials used in the two-component adhesive for insulating glass have strong adhesion, but no matter how strong the adhesion is, its characteristics can only be realized under specific conditions that meet the performance requirements, For the two-component adhesive we use, its * good adhesion (with glass and aluminum strip) is coated on the required coating part immediately after adding the specified amount of curing agent, so that it can complete the process from vulcanization to complete vulcanization at the coated part. If we apply the adhesive to the required part in the semi vulcanized state, the bonding strength will be greatly affected.